| 講演名 | 2012-12-01 Effect of Current Load on Fretting of Au-plated contacts , |
|---|---|
| PDFダウンロードページ |  PDFダウンロードページへ |
| 抄録(和) | |
| 抄録(英) | The fretting corrosion behavior of Au-plated contacts is studied at various current loads of 10, 100, 500 and 1000mA. The typical characteristics of the change in contact resistance with fretting cycles are investigated. The fretted surface is examined using scanning electron microscope and energy dispersive analysis of X-ray to assess the surface morphology, extent of oxidation and elemental distribution across the fretted zone. The degradation of contacts at different values of current is explained with reference to the ability of current to melt metal and breakdown oxide films. With larger amount of molten metal and area conducting current, the contacts at higher current load delay the time to reach failure, keep a relatively low contact resistance but surfer a severe fluctuation in contact resistance. The observed surface morphology reveals five typical regions within the fretted zone. |
| キーワード(和) | |
| キーワード(英) | Fretting / Contact resistance / Au-plated contacts / Current load / Fretting cycle / Surface characterization |
| 資料番号 | EMD2012-87 |
| 発行日 |
| 研究会情報 | |
| 研究会 | EMD |
|---|---|
| 開催期間 | 2012/11/23(から1日開催) |
| 開催地（和） | |
| 開催地（英） | |
| テーマ（和） | |
| テーマ（英） | |
| 委員長氏名（和） | |
| 委員長氏名（英） | |
| 副委員長氏名（和） | |
| 副委員長氏名（英） | |
| 幹事氏名（和） | |
| 幹事氏名（英） | |
| 幹事補佐氏名（和） | |
| 幹事補佐氏名（英） | |
| 講演論文情報詳細 | |
| 申込み研究会 | Electromechanical Devices (EMD) |
|---|---|
| 本文の言語 | ENG |
| タイトル（和） | |
| サブタイトル（和） | |
| タイトル（英） | Effect of Current Load on Fretting of Au-plated contacts |
| サブタイトル（和） | |
| キーワード(1)（和/英） | / Fretting |
| 第 1 著者 氏名（和/英） | / Wanbin Ren |
| 第 1 著者 所属（和/英） | School of Electrical Engineering and Automation, Harbin Inst. Of Tech. |
| 発表年月日 | 2012-12-01 |
| 資料番号 | EMD2012-87 |
| 巻番号（vol） | vol.112 |
| 号番号（no） | 332 |
| ページ範囲 | pp.- |
| ページ数 | 8 |
| 発行日 | |