| 講演名 | 2012-12-01 Effect of Lubricant on Lifetime of Au-plated Slip-Ring and Ag-Pd-Cu Brush System for Small Electric Power-2- , |
|---|---|
| PDFダウンロードページ |  PDFダウンロードページへ |
| 抄録(和) | |
| 抄録(英) | The authors have been investigating degradation process of Au plated slip ring and Ag-Pd-Cu brush system. In almost all cases the lifetime of the sliding system ends, when Au plating layer is worn out, the ring surface is oxidized to be black in color and contact resistance becomes very high. Further, the lifetime is very short without lubricant. So, the lubricant is very effective to make the lifetime longer. However, even with lubricant the lifetime is varied from about 1000 hours to almost 7000 hours in the past experiments. It is an important issue how the lubricant works on the lifetime of the system. In this paper the effect of lubricant on the degradation process of contact resistance is focused on. In the past tests the lubricant is supplied only once before the test. In this test the lubricant is regularly supplied almost every 1000 operation hours. Consequently, the operation more than 9000 hours is realized, which is the longest among tests so far. In addition the contact voltage drop stays almost constant around 50mV and after that contact voltage drop increase gradually until 5000 hours. According to the Element Analysis after the test the Ni base plating layer is totally exposed in many tracks. It means that the Au plating layer is gradually worn out probably at the stage of increasing voltage drop. In the previous tests the lifetime ended even when the Ni plating layer remained. So, the reason of long operation in this test is guessed to be that the lubricant not only decreases wear of ring and brush, but also suppresses oxidation of the Ni layer. |
| キーワード(和) | |
| キーワード(英) | slip ring / Au plating / Ni base plating / Ag-Pd brush / lifetime / lubricant |
| 資料番号 | EMD2012-84 |
| 発行日 |
| 研究会情報 | |
| 研究会 | EMD |
|---|---|
| 開催期間 | 2012/11/23(から1日開催) |
| 開催地（和） | |
| 開催地（英） | |
| テーマ（和） | |
| テーマ（英） | |
| 委員長氏名（和） | |
| 委員長氏名（英） | |
| 副委員長氏名（和） | |
| 副委員長氏名（英） | |
| 幹事氏名（和） | |
| 幹事氏名（英） | |
| 幹事補佐氏名（和） | |
| 幹事補佐氏名（英） | |
| 講演論文情報詳細 | |
| 申込み研究会 | Electromechanical Devices (EMD) |
|---|---|
| 本文の言語 | ENG |
| タイトル（和） | |
| サブタイトル（和） | |
| タイトル（英） | Effect of Lubricant on Lifetime of Au-plated Slip-Ring and Ag-Pd-Cu Brush System for Small Electric Power-2- |
| サブタイトル（和） | |
| キーワード(1)（和/英） | / slip ring |
| 第 1 著者 氏名（和/英） | / Hideki KITAJIMA |
| 第 1 著者 所属（和/英） | Nippon Institute of Technology |
| 発表年月日 | 2012-12-01 |
| 資料番号 | EMD2012-84 |
| 巻番号（vol） | vol.112 |
| 号番号（no） | 332 |
| ページ範囲 | pp.- |
| ページ数 | 6 |
| 発行日 | |