| Presentation | 2011-04-15 Degradation analysis of organic photovoltaioc cells for high durability Toshihiro YAMANARI, Yuji YOSHIDA, |
|---|---|
| PDF Download Page |  PDF download Page Link |
| Abstract(in Japanese) | (See Japanese page) |
| Abstract(in English) | For the practical use of organic photovoltaic cells (OPV), the high durability is much important feature. We focused on the degradation mechanism of OPV due to upgrade of the durability. In this study, we introduced a electroluminescence methods as a new degradation analysis for visualization of various defects. So, the inside defect structure of OPV was revealed in the initial stage of degradation.. |
| Keyword(in Japanese) | (See Japanese page) |
| Keyword(in English) | organic photovoltaic cells / degradation mechanism / electroluminescence / electrode oxidation |
| Paper # | SDM2011-5,OME2011-5 |
| Date of Issue |
| Conference Information | |
| Committee | SDM |
|---|---|
| Conference Date | 2011/4/8(1days) |
| Place (in Japanese) | (See Japanese page) |
| Place (in English) | |
| Topics (in Japanese) | (See Japanese page) |
| Topics (in English) | |
| Chair | |
| Vice Chair | |
| Secretary | |
| Assistant | |
| Paper Information | |
| Registration To | Silicon Device and Materials (SDM) |
|---|---|
| Language | JPN |
| Title (in Japanese) | (See Japanese page) |
| Sub Title (in Japanese) | (See Japanese page) |
| Title (in English) | Degradation analysis of organic photovoltaioc cells for high durability |
| Sub Title (in English) | |
| Keyword(1) | organic photovoltaic cells |
| Keyword(2) | degradation mechanism |
| Keyword(3) | electroluminescence |
| Keyword(4) | electrode oxidation |
| 1st Author's Name | Toshihiro YAMANARI |
| 1st Author's Affiliation | Photovoltaic Research Center, AIST() |
| 2nd Author's Name | Yuji YOSHIDA |
| 2nd Author's Affiliation | Photovoltaic Research Center, AIST |
| Date | 2011-04-15 |
| Paper # | SDM2011-5,OME2011-5 |
| Volume (vol) | vol.111 |
| Number (no) | 4 |
| Page | pp.pp.- |
| #Pages | 4 |
| Date of Issue | |