| 講演名 | 2010-08-26 An Innovation of Calcium Zeolite Catalyst Synthesis from Eggshell via Sol-gel Process , |
|---|---|
| PDFダウンロードページ |  PDFダウンロードページへ |
| 抄録(和) | |
| 抄録(英) | Calcium zeolite type A (CaNaAlSi_2O_7) called soda melilite with the molar ratio of CaO:Al_2O_3:Na_2O:SiO_2 is 1:1:2:8 was prepared by the sol-gel process and calcined at 300℃ for 1 h. The CaNaAlSi_2O_7 catalysts have the N_2 adsorption-desorption isotherms and good electrical properties. The specific surface area, total pore volume, and average pore diameter are 55.15 m^2/g, 0.5127, and 371.90 A°, respectively by Braunauer Emmett Teller (BET). The dielectric constant, electrical conductivity, and loss tangent are 46.5785, 5.2360x10^<-3> (Ω.m)^<-1>, and 2.7540, measured at room temperature and at 1000 kHz (1MHz), respectively. The transmission electron microscopy (TEM) images of the samples show that good dispersion and uniform particles with an average diameter of about 0.5 nm are prepared. |
| キーワード(和) | |
| キーワード(英) | Calcium zeolite catalysts / Sol-gel process / Eggshell / Dielectric material |
| 資料番号 | EMD2010-32,CPM2010-48,OPE2010-57,LQE2010-30 |
| 発行日 |
| 研究会情報 | |
| 研究会 | CPM |
|---|---|
| 開催期間 | 2010/8/19(から1日開催) |
| 開催地（和） | |
| 開催地（英） | |
| テーマ（和） | |
| テーマ（英） | |
| 委員長氏名（和） | |
| 委員長氏名（英） | |
| 副委員長氏名（和） | |
| 副委員長氏名（英） | |
| 幹事氏名（和） | |
| 幹事氏名（英） | |
| 幹事補佐氏名（和） | |
| 幹事補佐氏名（英） | |
| 講演論文情報詳細 | |
| 申込み研究会 | Component Parts and Materials (CPM) |
|---|---|
| 本文の言語 | ENG |
| タイトル（和） | |
| サブタイトル（和） | |
| タイトル（英） | An Innovation of Calcium Zeolite Catalyst Synthesis from Eggshell via Sol-gel Process |
| サブタイトル（和） | |
| キーワード(1)（和/英） | / Calcium zeolite catalysts |
| 第 1 著者 氏名（和/英） | / Nuchnapa TANGBORIBOON |
| 第 1 著者 所属（和/英） | Materials Engineering Department, Faculty of Engineering, Kasetsart University |
| 発表年月日 | 2010-08-26 |
| 資料番号 | EMD2010-32,CPM2010-48,OPE2010-57,LQE2010-30 |
| 巻番号（vol） | vol.110 |
| 号番号（no） | 179 |
| ページ範囲 | pp.- |
| ページ数 | 4 |
| 発行日 | |