講演名	1999/11/9 Adding SiO_2 to Increase Coercivity And Squareness Ratio of Ba Ferrite Films for Perpendicular Magnetic Recording Media ,
PDFダウンロードページ	PDFダウンロードページへ
抄録(和)
抄録(英)	In this study, SiO_2 added Ba ferrite (BaM:SiO_2) films were prepared. BaM:SiO_2 films exhibited H_ as high as 4.2 kOe and squareness ratio of 0.83, although M_s decreased to 80% of that of simple Ba ferrite films. Angular dependence of coercivity H_c and remanent coercivity H_r were investigated o explain the magnetization reversal mechanism. Intergranular interactions in the films were also evaluated. The magnetization reversal mode of Ba ferrite films with and without SiO_2 additives is not coherent rotation but seems like curling mode. SiO_2 additives did not decrease perpendicular anisotropy of grains apparently, but seemed to prevent the expansion of reversed domain in the magnetization reversal process of curling just like some effects of pinning.
キーワード(和)
キーワード(英)	Ba ferrite / film / adding SiO_2 / coercivity / magnetization reversal
資料番号	MR99-38
発行日

研究会情報
研究会	MR
開催期間	1999/11/9(から1日開催)
開催地（和）
開催地（英）
テーマ（和）
テーマ（英）
委員長氏名（和）
委員長氏名（英）
副委員長氏名（和）
副委員長氏名（英）
幹事氏名（和）
幹事氏名（英）
幹事補佐氏名（和）
幹事補佐氏名（英）

講演論文情報詳細
申込み研究会	Magnetic Recording (MR)
本文の言語	ENG
タイトル（和）
サブタイトル（和）
タイトル（英）	Adding SiO_2 to Increase Coercivity And Squareness Ratio of Ba Ferrite Films for Perpendicular Magnetic Recording Media
サブタイトル（和）
キーワード(1)（和/英）	/ Ba ferrite
第 1 著者 氏名（和/英）	/ J. Feng
第 1 著者 所属（和/英）	Department of Physical Electronics, Tokyo Institute of Technology
発表年月日	1999/11/9
資料番号	MR99-38
巻番号（vol）	vol.99
号番号（no）	420
ページ範囲	pp.-
ページ数	6
発行日