| 講演名 | 1999/2/26 Compositional variation of magnetoresistance characteristics in NiFe/Cu/Co spin valve thin films , |
|---|---|
| PDFダウンロードページ | PDFダウンロードページへ |
| 抄録(和) | |
| 抄録(英) | Giant magnetoresistance (GMR) characteristics of NiFe/Cu/Co spin valve thin films, which were formed on Cu/Si(111, 4 degree tilt-cut) templates by a 3-gun magnetron sputtering system, have been investigated as a function of composition in NiFe layer. It was found that R-H curves of these thin films change drastically with the composition in NiFe layer so that perfectly square R-H curves were obtained at 4 : 1 atomic ratio of Ni : Fe and sloped R-H curves at zero external magnetic fields were obtained at other atomic ratios of Ni : Fe. The change of R-H curves could be understood by a transition of magnetic anisotropy in NiFe layer with the compositional variation. Analvsis of crystal structures and preferred orientations by pole figure measurement indicate that the changes of magnetic anisotropy and GMR characteristics are originated from the variation of magnetoelastic effect of thin films. It was believed that these various GMR characteristics could increase the potentials of NiFe/Cu/Co spin valve thin films for recently researched magnetic devices. |
| キーワード(和) | |
| キーワード(英) | NiFe/Cu/Co spin valve thin films / GMR / NiFe / composition |
| 資料番号 | MR-98-91 |
| 発行日 |
| 研究会情報 | |
| 研究会 | MR |
|---|---|
| 開催期間 | 1999/2/26(から1日開催) |
| 開催地（和） | |
| 開催地（英） | |
| テーマ（和） | |
| テーマ（英） | |
| 委員長氏名（和） | |
| 委員長氏名（英） | |
| 副委員長氏名（和） | |
| 副委員長氏名（英） | |
| 幹事氏名（和） | |
| 幹事氏名（英） | |
| 幹事補佐氏名（和） | |
| 幹事補佐氏名（英） | |
| 講演論文情報詳細 | |
| 申込み研究会 | Magnetic Recording (MR) |
|---|---|
| 本文の言語 | ENG |
| タイトル（和） | |
| サブタイトル（和） | |
| タイトル（英） | Compositional variation of magnetoresistance characteristics in NiFe/Cu/Co spin valve thin films |
| サブタイトル（和） | |
| キーワード(1)（和/英） | / NiFe/Cu/Co spin valve thin films |
| 第 1 著者 氏名（和/英） | / Hyeong-Jun Kim |
| 第 1 著者 所属（和/英） | School of Materials Science and Engineering , Seoul National University |
| 発表年月日 | 1999/2/26 |
| 資料番号 | MR-98-91 |
| 巻番号（vol） | vol.98 |
| 号番号（no） | 621 |
| ページ範囲 | pp.- |
| ページ数 | 6 |
| 発行日 | |